樂泰 HYSOL KL 1000-3A provides the lowest cost ofownership with superior moldability and reliability.樂泰 HYSOL KL 1000-3A meets UL 94 V-0 Flammability at 3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 23Spiral Flow, @ 175°C, cm 80Shelf Life:@ 5oC, days 365TYPICAL PROCESS DATA
HandlingPreheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time: Conventional mold, seconds 10 to 18Automold, seconds 4 to 10Curing Time, @ 175oC: Conventional mold, seconds 50 to 120Automold, seconds 50 to 80Post Cure @ 175°C, hours 4 to 6樂泰 HYSOL KL 1000-3A has been formulated to provide thebest possible moldability and as wide a molding latitude as possible.
Although molding and curing conditions will vary from situation tosituation, recommended starting ranges are shown above.StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers. After removal from cold storage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15 kg carton box is 24 hours.
樂泰 HYSOL KL 1000-3A提供*低的擁有成本，具有出色的成型性和可靠性.樂泰 HYSOL KL 1000-3A符合UL 94 V-0易燃性厚度為3.175mm。
固化材料的特性特性時間@ 175°C秒秒23螺旋流@ 175°C cm 80Shelf壽命@5oC365天工藝數據處理預熱溫度：常規模具，°C 80至100Automold，秒0至5成型溫度，℃150至195壓鑄壓力，Kg /cm240至100轉印時間：常規模具，秒10至18Auoldold，秒4至10℃時間，@175oC：常規模具，秒50至120Automold，秒50至80后固化@ 175°C，小時4至6樂泰 HYSOL KL 1000-3A已配制成盡可能提供可塑性和成型寬度。
盡管成型和固化條件將不同的情況，建議的起始范圍如上所示。儲存產品在未開封的容器中，在干燥的位置。儲存信息可能在產品容器標簽上指示。
粉末儲存 - 粉末或預制件應存放在5oC以下，密閉容器中 |
 |
|