樂泰 HYSOL GR 2720 is a green epoxy based moldingcompound designed for the encapsulation of passivecomponents.
This material is an excellent candidate for the
molding of pressure sensitive components.樂泰 HYSOL GR 2720 meets UL 94 V-0 Flammability at6.35mm thickness.TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 19Spiral Flow, @ 175°C, inches 38Shelf Life:@ -18oC, months 6
Hot Hardness,Shore-D@ 175°C, 90 seconds 90TYPICAL PROCESS DATAHandling
Preheat Temperature , °C 80 to 95Molding Temperature, °C 140 to 180Transfer Pressure, Kgf/cm2 40 to 85Transfer Time, seconds 6 to 15Curing Time, 3 mm section:Conventional mold:@ 175oC, seconds 70 to 90Automold:@ 175oC, seconds 50 to 70Post Cure @ 175°C, hours 2 to 6StorageStore product in the unopened container in a dry location.
Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at -4oCor below, in closed containers.
After removal from cold torage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15kg carton box is 24 hours.
樂泰 HYSOL GR 2720是一種綠色環氧基成型復合材料，專為封裝被動元件而設計。
這種材料是很好的候選人壓力敏感部件的成型.
樂泰 HYSOL GR 2720符合UL 94 V-0可燃性，厚度為6.355mm。固化材料的特性固體時間@ 175°C，秒19螺旋流，@ 175°C，英寸38Shelf壽命：@-18oC，月6熱硬度，Shore-D @ 175°C，90秒90工藝流程數據處理預熱溫度°C 80至95模具溫度°C 140至180轉印壓力Kgf /cm240至85轉印時間秒6至15烘烤時間3毫米截面：常規模具：@ 175℃，秒70至90Automold：@ 175℃，秒50至70次固化@ 175°C，小時2至6個儲存在未開封的容器中的產品在干燥的位置。
儲存信息可能在產品容器標簽上顯示。
粉末儲存 - 粉末或預型件應儲存在-4oC以下，密閉容器。
從寒冷除去后儲存時，必須在密封容器中允許材料進入室溫，以避免水分污染。
建議的等待時間為標準15kg紙箱是24小時。 |
 |
|