樂泰 HYSOL KL 5000-HT epoxy molding compounddelivers outstanding performance and ease of use.
樂泰 HYSOL KL 5000-HT meets UL 94 V-0 Flammabilityat 3.175mm thickness.TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 32 Spiral Flow, @ 175°C, cm 60Shelf Life:@ 5oC, months 12TYPICAL PROCESS DATAHandling Preheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100TransferTime:Conventional mold, seconds 10 to 25Automold, seconds 4 to 15Curing Time, @ 175oC:Conventional mold, seconds 70 to 120Automold, seconds 60 to 90Post Cure @ 175°C, hours 4 to 6 StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers. After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination. The suggested waiting time for a standard 15kg carton box is 24 hours.
樂泰 HYSOL KL 5000-HT環(huán)氧樹脂成型復(fù)合材料具有出色的性能和易用性.
樂泰 HYSOL KL 5000-HT符合UL 94 V-0 Flammabilityat 3.175mm厚度。
固化材料的特性特性時(shí)間@ 175°C秒秒32螺旋流，@ 175°C，cm 60Shelf壽命：@5oC，月12個(gè)工藝流程數(shù)據(jù)處理預(yù)熱溫度：常規(guī)模具，80至100Automold，秒0至5模具溫度，℃150至195Molding壓力，Kg / cm 2 40至100轉(zhuǎn)印時(shí)間：常規(guī)模具，秒10至25Automold，秒4至15烘烤時(shí)間，@ 175℃：常規(guī)模具，秒70至120Automold，秒60至90后固化175℃，小時(shí)4至6StorageStore產(chǎn)品在未開封的容器中，在干燥的位置。
存儲信息可能在產(chǎn)品容器標(biāo)簽上指示。
粉末儲存 - 粉末或預(yù)制件應(yīng)存放在5oC以下，密閉容器中。從冷藏箱中取出后，必須在密封容器中使材料達(dá)到室溫，以避免水分污染。
標(biāo)準(zhǔn)15kg紙箱的建議等待時(shí)間為24小時(shí)。 |