樂泰® EA 9460™ is a thixotropic, modified, two-component epoxy adhesive formulated for ease of use as well for a good balance of properties. This two-part adhesive is formulated to give very high peel strength coupled with excellent shear strength. The flexibility of the cured adhesive makes it useful for bonding dissimilar substrates. Recommended substrates include metals, engineering thermoplastics, and thermoset laminates such as sheet molding compound (SMC) without the use of primers.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Resin:
Specific Gravity @ 25 °C 1.35
Viscosity, Brookfield - HB, 25 °C, mPa•s (cP):
Spindle 6, speed 20 rpm 150,000 to 300,000LMS
Weight Per Gallon, lbs/gal 11.3
Flash Point - See SDS
Hardener:
Specific Gravity @ 25 °C 1.31
Viscosity @ 25°C, mPa•s (cP) 100,000 to 250,000
Weight Per Gallon, lbs/gal 10.9
Flash Point - See SDS
Mixed:
Specific Gravity @ 25 °C 1.33
Viscosity @ 25°C, mPa•s (cP) 150,000 to 250,000
Peak Exotherm Temperature, °C, 93
Weight Per Gallon, lbs/gal 11.1
Pot life @ 25 °C, minutes 40 to 65LMS
TYPICAL PROPERTIES OF CURED MATERIAL
Cured @ 25 °C except where noted
Physical Properties:
Shore Hardness, ISO 868, Durometer D:
Cured for 2 hours @ 60 °C ≥75LMS
Glass Transition Temperature, °C 68
Elongation, ISO 527-2, % 3.5
Tensile Strength, ISO 527-2 N/mm2 30.3
(psi) (4,400)
Tensile Modulus, ISO 527-2 N/mm2 2,758
(psi) (400,000)
樂泰®EA 9460™是湯姆遜，改性，環(huán)氧膠粘劑的配方為兩維草of use as well for a good balance of置業(yè)。這兩方面是非常高的膠粘劑配方給皮強度耦合以及優(yōu)秀的剪切強度。the Flexibility of the固化膠粘劑使它useful for接合異種基質(zhì)。建議包括金屬基質(zhì)，工程thermoplastics，and thermoset laminates such as薄板成型復合（SMC）without the use of引物。
uncured材料的典型性能
樹脂：
比重：25℃1.35
粘度，Brookfield，HB，25℃，mpa•s（CP）：
主軸6速20轉(zhuǎn)300000lms 150000 to
體重每加侖，磅/加侖11.3 |
免責聲明：以上所展示的信息由會員自行提供，內(nèi)容的真實性、準確性和合法性由發(fā)布會員負責，www.qy6.com對此不承擔任何責任。如有侵犯您的權(quán)益，請來信通知刪除。